US Patent 5273571 - Nonmagnetic nickel tungsten cemented carbide compositions and articles made from the same(2)
SUMMARY OF THE INVENTION
The present invention relates to a nickel tungsten cemented carbide composition and articles made therefrom which has a nonmagnetic behavior independent of the free carbon level of the composition. The composition comprises from about 60 to about 98 percent by weight of a carbide of the elements selected from the group consisting of Group IVB, Group VB, Group VIB of the periodic table, and mixtures thereof, from about 0.2 to about 4.0 percent by weight chromium; and the balance nickel.
The composition further includes up to about 4.0 percent by weight alloying elements selected from the group consisting of molybdenum, copper, aluminum, silicon and mixtures thereof. When an alloying element is present in an amount of up to 1percent by weight of the composition, the alloying element may be selected from the group consisting of copper, aluminum, silicon and mixtures thereof. The composition may posses a free carbon level as high as CO6 as measured by ASTM procedure B 276-79. It is surprising that the amount of chromium necessary to render the composition nonmagnetic decreases as the level of free carbon decreases. Indeed, no brittle eta phase is created by carbon depletion of the WC. The composition exhibits a non magnetic behavior which is defined as a saturation magnetization in the range of less than or equal to 5 emu/g.
FIG. 1 is a graph showing the saturation magnetization of the sintered samples as a function of Cr3C2 content.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
The present invention is a nickel tungsten cemented carbide composition which has a nonmagnetic behavior independent of the of the free carbon level of the composition. The composition is comprised of from about 60 to about 98 percent by weight of a carbide of the elements selected from the group consisting of Group IVB, Group VB, Group VIB of the periodic table, and mixtures; thereof from about 0.2 to about 4.0 percent by weight chromium; and the balance nickel. The composition optionally further includes up to about 4.0 percent by weight of an alloying element selected from the group consisting of molybdenum, copper, aluminum, silicon and mixtures thereof. Preferably, the alloying element is molybdenum. However, the alloying element may also be selected from the group consisting of copper, aluminum, silicon and mixtures thereof, present in amounts up to about 1 percent by weight of the composition. The composition of the present invention exhibits nonmagnetic properties even when the free carbon level is as high as CO6 as measured by ASTM procedure B 276-79.
It has been discovered that the amount of chromium necessary to render the composition nonmagnetic decreases as the level of free carbon decreases.
The composition of the present invention is considered to exhibit non magnetic behavior when it has a saturation magnetization in the range of less than or equal to 5 emu/g, and preferably, approaching 0 emu/g.
The composition of the present invention is very useful in a situation where a non magnetic material is necessary. For example, the present invention is well suited for wear parts useful in electronic applications, and further as punches to deep draw aluminum cans where the punch, if it acquired magnetism, would interfere with electronic sensors. This property allows an operator to automate the can manufacturing process without fear of shut down due to sensor failure.
As can be seen in FIG. 1, the saturation magnetization of NiWC cemented carbides as a function of chromium carbide declined as the amount of chromium carbide added was increased.
Those skilled in the art recognize that the following examples are illustrative of various aspect of the invention and many modifications will be apparent without departing from the scope and spirit of the invention.
EXAMPLES
Sintered Ni-WC based cemented carbide samples were prepared using means well known to those of ordinary skill in the art. The following Ni-WC based cemented carbide samples are given in percent by weight. All samples were prepared in the same manner using standard cemented carbide technology involving milling of powder blends, consolidation and vacuum sintering.
TABLE 1 ______________________________________ (1) 12% Ni, 0.1% C, balance WC (2) 12% Ni, 0.1% C, 0.6% Cr3C2, balance WC (3) 12% Ni, 0.1% C, 1.20% Cr3C2, balance WC (4) 12% Ni, 0.07% C, 1.80% Cr3C2, balance WC (5) 12% Ni, 0.07% C, 2.40% Cr3C2, balance WC ______________________________________
As indicated above, the Cr in the samples was introduced through Cr3C2 additions. Those skilled in the art recognize that Cr additions can also be made via elemental Cr additions, or by the use of master alloys containing Cr. The Cr percentage in the above samples 1 through 5 was roughly 0. 0.5%, 1.0%, 1.5% and 2.0% respectively. The sintered samples were prepared via ball milling of powder blends, consolidation of the milled powder, followed by vacuum sintering. Deliberate carbon additions were made to demonstrate that nonmagnetic behavior could be achieved even in the presence of free carbon.
TABLE 2 ______________________________________ The following samples were prepared in the same manner as those of Table 1. The free carbon level measured according to ASTM procedure B276-79. Free Carbon Composition Level ______________________________________ (1) 12% Ni, 0.1% C, WC balance CO1 (2) 12% Ni, 0.1% C, 0.6% Cr3C2, WC Balance CO4 (3) 12% Ni, 0.1% C, 1.8% Cr3C2, WC Balance CO4 (4) 12% Ni, 0.07% C, 1.8% Cr3C2, WC Balance CO6 (5) 12% Ni, 0.07% C, 2.4% Cr3C2, WC Balance CO6 ______________________________________
Table 2 shows that all samples retained a significant levels of free carbon. Each sample retained a nonmagnetic nature in spite of the free carbon level in the sample. In particular, sample 5 was essentially non magnetic in spite of the relatively high free carbon level.
If you need any more details of the above news and/or products, please visit Chinatungsten Online, or contact us directly.
Disclaimer: The article is only reflecting the opinions of the author. We have no responsibility to prove the originality and authenticity of the content, words and/or pictures. You readers should just take it as reference and check the details by yourselves. And the content is not a suggestion for investment decision. The investor takes his or her own risks if he or she operates accordingly. If you have any dissent about the contents above, please contact the relevant author, or the webmaster. We will try our best to assist the dealing of the related issues. Thanks for your visit and cooperation.
|